Figuratus, Flat, Quadratus, Rotundus, Fine, Plated et Bare Wire ASTM A167, AMS 5523
Applicationem
Fornacis partes
Calor Commutatores
Paper Mill Equipment
Exhauriunt Partes in Gas Turbines
Jet Engine Parts
Oleum Refinery Equipment
Typical Chemia
| Carbon | 0.080 max |
| Manganese | 2.00 max |
| Pii | 0.75 max |
| Chromium | 24.00- 26.00 |
| Nickel | 19.00- 22.00 |
| Molybdenum | 0.75 max |
| Phosphorus | 0.003 max |
Corporalia Properties
| Density | 0.29 lbs/in³ 9.01 g/cm³ |
| Resistivity electrica | microhm-in (microhm-cm) |
| 68°F (20°C) | 37.0 (94.0) |
| Imprimis Caloris | BTU/lb/°F (kJ/kg•K) |
| 32-212°F (0-100°C) | 0.12 (0.50) |
| Scelerisque Conductivity | BTU/hr/ft²/ft/°F (W/m•K) |
| Ad 212°F (100°C) | 8.0 (13.8) |
| In 932°F (D°C) | 10.8 (18.7) |
| Medium Coefficiens Scelerisque Expansion | in/in/°F (μm/m•K) |
| 32-212°F (0-100°C) | 8.0 x 10 (14.4) |
| 32-600°F (0-315°C) | 9.3 x 10 (16.7) |
| 32-1000°F (0-538°C) | 9.6 x 10 (17.3) |
| 32-1200°F (0-649°C) | 9.7x 10 (17.5) |
| Modulus Elasticitatis | KSI (MPa) 29.0 x 10³ (200 x 10³) in contentione 11.2 x 10³ (78 x 10³) in torsione |
| Magnetic Permeability | H = 200 Oersteds |
| Annealed | < 1.02 max |
| Exustio Range | °F (°C) 2550 - 2650 (1399-1454) |
Mechanica Properties
Mechanica Properties At volutpat Temperature
| POTESTAS | ANNEALED |
| Ultima distrahentes Fortitudo | 75 KSI min (515 MPA min) |
| Cede fortitudo (0.2% offset) | 30 KSI min (205 MPA min) |
| Prolongatio | 40% min duritia Rb 95 max |
| Properties | Temperata 310S suppleri possunt in variis conditionibus temperatis revolutis. |
Ulbrich Technical Service Contactus pro details.
Corrosio Resistentia
Refer ad NACE (Consociatio Nationum Corrosionis Engineers) pro commendatione.
Proprietates Temperatae Alloy 310S frigidae involvi possunt ad obtinendas proprietates temperamenti quae requiruntur a certis clientibus et/vel fabricandis requisitis. Contactus Ulbrich filum pro details.
Formae
Continua Coils Incidere ad longitudinem Subtilitas cutting
Frigus Formans Alloy 310S ductilem bonam habet et facile formari, signari et trahi potest.
Curatio Caloris Alloy 310S durari potest nisi frigore operationis.
Welding optimos proventus referuntur ad: SSINA scriptor "Welding Steels et Alii coniungentes"
Methodi".
Limitatio reatus et Disclaimer Warranty: nullo eventu Ulbrich Steels et Metalla Specialia, Inc., tenebitur damna quaevis ex usu percontationum in hoc documento comprehensae vel aptum ad "applicationes" notatas. Informationes et notitias accurate pro nostra scientia provisas credimus, sed omnia notitia valores typicos tantum considerantur. Ad referentiam et informationem generalem destinatur et non commendatur ad specificationem, designationem vel ad technologiam proposita. Ulbrich nullam ponit tacitam vel expressam warantum quoad creationem vel accurationem notitiis in hoc documento.