High Precision Alloy
High Temperature Alloy
◆1J50 habet ansam hysteresis rectangulam et altam satietatem inductionis magneticae.Maxime adhibetur in agro magnetico augente, gyros suffocant, gyros rectificantes, et machinamenta computatralia operantia in campis mediis magneticis.
◆1J79 altam initialem magneticam permeabilitatem habet, ac variis transformatoribus, transformatoribus, amplificantibus magneticis, coros suffocatis et clypeis magneticis in campis magneticis infirmis laborantibus.
◆3J53 humilis frequentiam temperaturae coefficiens in latitudine -40-80°C habet, et pro vibratore in colum mechanica, calamus vibrationis et aliis componentibus adhibetur.
◆4J29(F15) expansionem coefficiens linearem habet similem cum vitro duro intra ambitum quendam temperatum et ad adaptationem vitri duri in vacuo industria adhibito.
◆4J36 peculiaris est extensio ferri-nickel mixturae humilitatis cum coëfficiente ultra-low expansione, quae in ambitu requirit coëfficientem expansionem valde humilem.
◆4J42 maxime adhibetur in fabricandis electricis machinis vacuum, instrumentis subtilitatis, instrumentis geodeticis astronomicis cum summa stabilitate requisita, etc.
Chemical compositione
| Gradus | C | Si | Mn | S | P | Cr | Ni | Mo | Cu | Fe | Al | Co | Ti |
| non major | |||||||||||||
| 1J50 | 0.03 | 0.15～0.3 | 0.3～0.6 | 0.02 | 0.02 | - | 49.5～50.5 | . | ≤0.2 | basis | - | - | - |
| 1J79 | 0.03 | 0.3～0.5 | 0.6～1.1 | 0.02 | 0.02 | - | 78.5～80.5 | 3.8～4.1 | ≤0.2 | basis | - | - | - |
| 3J53 | 0.05 | 0.8 | 0.8 | 0.02 | 0.02 | 5.2～5.8 | 41.5～43 | 0.7～0.9 | - | basis | 0.5～0.8 | - | 2.3～2.7 |
| 4J29 | 0.03 | 0.3 | 0.5 | 0.02 | 0.02 | 0.2 | 28.5～29.5 | 0.2 | ≤0.2 | basis | - | 16.8～17.8 | - |
| 4J36 | 0.05 | 0.3 | 0.2～0.6 | 0.02 | 0.02 | - | 35～37 | . | - | basis | - | - | - |
| 4J42 | 0.05 | 0.3 | 0.8 | 0.02 | 0.02 | - | 41.5～42.5 | - | - | basis | ≤0.1 | ≤1.0 | - |
Alloy res minimum
| Gradus | Varietas | Magnae possessiones | ||
| Coepi permeability uo(MH/m) | Maximum Permeability (Uh / m) | Coactio Hc(A/m) | ||
| 1J79 | Frigus involutus habena | ≥31 | ≥250 | ≤1.2 |
| lignum filum tabula | ≥25 | ≥125 | ≤2.4 | |
| 1J50 | Frigus involutus habena | ≥3.8 | ≥62.5 | ≤9.6 |
| Composuerunt (advolvit) vectes | ≥3.1 | ≥31.3 | ≤14.4 | |
| Gradus | status | Modulus Elasticus E(Mpa) | distrahentes vires b (N / m) | duritia Hv* |
| 3J53 | frigus opus + canus | 190000～215600 | 1170～1760 | 400～480 |
| Gradus | Mediocris Linearibus Expansion Coefficiens (10-6) | ||||||
| 20～100℃ | 20～300℃ | 20～400℃ | 20～450℃ | 20～500℃ | 20～530℃ | 20～600℃ | |
| 4J29 | - | - | 4.6～5.2 | 5.1-5.5 | - | - | - |
| 4J50 | - | 9.2～10 | 9.2～9.9 | - | - | - | - |
| 4J36 | - | ≤1.5 | - | - | - | - | - |
| 4J42 | 5.5 | 4.6 | 5.8 | 6.7 | 7.6 | - | 9.1 |