High Temperature Alloy
High Temperature Alloy
◆ GH2132 (incoloyA-286/S66286) bonum altiore effectus habet et altum cedere modum.Ponitur pro turbines discorum, corporum anulorum, brackets welditatum et recompensationum partium materiarum infra DCC °C.
GH3030 mixturae structuram stabilem habet, minus senescentis, bonam oxidationis resistentiam.Cubicula combustionis apta est et afterburners infra 800 °C.
◆ GH3128 bonum comprehensivum effectum, altam durabilitatem, bonam oxidationis resistentiam, stabilitatem sistens bonam et functionem bonam glutinosam habet, et maxime ad cameram combustionis et partium combustionis machinam turbinem cum operante temperie 950°C adhibita est.
◆ GH4145 (inconlx-750/N07750) satis virium habet, resistentia corrosionis et resistentiae oxidationis infra 980°C.Materia altae fortitudinis fontium praefertur et apta est ad diaphragmata elastica et elasticas schedas signandas apta.
◆GH4169 (N07718/inconel718) austenite structuram habet, et "Y" phase formata post praecipitationem obdurationem praestantes proprietates mechanicas facit.Resistentia caliditas late in variis locis usus est.
◆GH4080A (N07080/Nimonic80A)Z sufficientem caliditatem habet ad 700-750°C et ad resistentiam oxygenii bonam infra 900°C.Hoc speciale stannum aptum est pro agris altae virium et corrosionum resistentia requirentium.
◆GH3044 Combustio principalis camerae et afterburner partium, calor scutorum, dux vanes, etc.
◆ GH4080A resistentia serpat et resistentia oxidationis in visibilibus 650-850°C.
◆ GH2136 bonum altiore effectus, stabilis structuram post diuturnum usum, bonam oxidationis resistentiam, parvam expansionem linearem coefficiens, facilem glutino et formans habet.
◆ GH2036 Turbine disc, calo scuta, annulos retentis, annulos, clavos ferentes, etc. infra DCL °C.
◆ GH4738 apta est ad faciendas discorum turbines, telas laborantes, fastigium summus temperatus, fistulae flammae, spicula et turbines, etc.
Chemical compositione
Gradus | C | Si | Mn | S | P | Cr | Co | W | Mo | Ti | Al | Fe | Ni | alius |
non major | ||||||||||||||
GH2132 | 0.08 | 1 | 2 | 0.02 | 0.03 | 13.5~16 | . | . | 1~1.5 | 1.75~2.35 | ≤0.4 | basis | 24~27 | B:0.001~0.01 V:0.1~0.5 |
GH3030 | 0.12 | 0.8 | 0.7 | 0.02 | 0.03 | 19~22 | . | . | . | 0.15~0.35 | ≤0.15 | ≤1.5 | basis | . |
GH3128 | 0.05 | 0.8 | 0.5 | 0.013 | 0.013 | 19~22 | . | 7.5~9 | 7.5~9 | 0.4~0.8 | 0.4~0.8 | ≤2.0 | basis | B≤0.005 Ce≤0.05 Zr≤0.06 |
GH4145 | 0.08 | 0.5 | 1 | 0.01 | 0.014 | 14~17 | ≤1 | . | . | 2.25~2.75 | 0.4~1 | 5~9 | ≥70 | Nb:0.7~1.2 |
GH4169 | 0.08 | 0.35 | 0.35 | 0.014 | 0.014 | 17~21 | ≤1 | . | 2.8~3.3 | 0.65~1.15 | 0.2~0.8 | manete | 50~55 | Cu≤0.3 Nb4.75~5.5 Mg≤0.1 B≤0.006 |
GH4080A | 0.04~0.1 | 1 | 1 | 0.014 | 0.02 | 18~21 | ≤2 | . | . | 1.8~2.7 | 1~1.8 | - | ≥65 | Cu≤2 B≤0.006 |
GH3044 | 0.1 | 0.8 | 0.5 | 0.013 | 0.013 | 23.5~26.5 | - | 13~16 | ≤1.5 | 0.3~0.7 | ≤0.5 | ≤4.0 | basis | Cu≤0.07 |
GH2136 | 0.06 | 0.75 | 0.35 | 0.025 | 0.025 | 13~16 | - | - | 1~1.75 | 2.4~3.2 | ≤0.35 | basis | 24.5~28.5 | B:0.005~0.025 V:0.01~0.1 |
GH2036 | 0.34~0.4 | 0.3~0.8 | 7.5~9.5 | 0.03 | 0.035 | 11.5~13.5 | - | - | 1.1~1.4 | ≤0.12 | - | basis | 7~9 | V:1.25~1.55 Nb:0.25~0.5 |
GH4738 | 0.03~0.1 | 0.15 | 0.1 | 0.014 | 0.014 | 18~21 | 12~15 | - | 3.5~5 | 2.75~3.25 | 1.2~1.6 | ≤2.0 | basis | B:0.003~0.01 Zr:0.02~0.08 |
Alloy res minimum
status | RmN vires distrahentes / m㎡ | Rp0.2N / m㎡ | Prolongatio, sicut% | Brinell duritia HB |
Solutio curatio | 610 | 270 | 30 | ≤321 |
Solutio curatio | 650 | 320 | 30 | - |
Solutio curatio | 735 | 340 | 40 | - |
Solutio curatio | 910 | 550 | 25 | ≤350 |
Solutio curatio | 965 | 550 | 30 | ≤363 |
Solutio curatio | 845 | 340 | 48.5 | . |
Solutio curatio | 920 | 550 | 25 | . |
Solutio curatio | 950 | 700 | 20 | . |
Solutio curatio | 850 | 600 | 15 | . |
Solutio curatio | 1111 | 741 | 21.5 | 24.5 |